Method for coating a sliding element and sliding element, in particular a piston ring or cylinder liner of an internal combustion engine

ABSTRACT

In a method for coating a sliding element, in particular a piston ring or a cylinder liner of an internal combustion engine, DLC phases are embedded into a hard material layer as said hard material layer is deposited. A sliding element, such as a piston ring or a cylinder liner of an internal combustion engine, comprises a hard material layer with embedded DLC phases.

TECHNICAL FIELD

The invention relates to a method for coating a sliding element, in particular a piston ring or a cylinder liner of an internal combustion engine, and a sliding element.

Piston rings are used in internal combustion engines in order to provide as perfect a sealing as possible between the piston that moves up and down and the cylinder wall. Furthermore, piston rings serve to wipe off the oil located on the cylinder wall and to maintain the usability of the oil for lubrication. The fundamental requirements placed on piston rings are the lowest possible friction and the longest possible service life under the, in part, extreme conditions during the operation of an internal combustion engine. This implies a wear behavior in which the piston ring meets the requirements placed on it as long as possible. The same applies to the wear behavior of cylinder liners with which the piston rings are in sliding contact.

PRIOR ART

WO 2007/020139 A1 describes a substrate that may be a piston ring, having an adhesive layer, an intermediate layer of tetrahedral carbon, and an outer layer of amorphous carbon.

DE 10 2005 063 123 B3 of applicant pertains to a sliding element, for example a piston ring which comprises a wear layer and a run-in layer.

REPRESENTATION OF THE INVENTION

The object underlying the invention is to provide a method for coating a sliding element, in particular a piston ring or a cylinder liner of an internal combustion engine, by which the requirements with regard to both the friction values and the service life are taken into account. Furthermore, a sliding element is supposed to be provided in which the friction values and a long service life are combined in an advantageous manner.

This object is solved, on the one hand, by the method described in claim 1.

According to this, a sliding element, in particular a sliding element of an internal combustion engine, e.g. a piston ring or a cylinder liner, is coated by deposition of a hard material layer. According to the invention, DLC phases are embedded in the hard material layer during the deposition, or in other words parallel thereto. The method according to the invention therefore differs from previously known methods in that the DLC coating is not carried out “on” the hard material layer and/or in a separate coating process, but in parallel and preferably simultaneously with the deposition of the hard material layer such that the described embeddings are formed. The embedding of the DLC phases can also be referred to as “in situ incorporation”. It could be found in tests that an advantageous friction behavior is achieved by the parallel presence of the hard material phases and the DLC phases. Furthermore, an advantageous wear behavior could be found. In other words, wear is in a range which ensures a service life in accordance with the requirements. The embedding of the DLC phases moreover makes it possible to provide the hard material layer with different properties along its thickness in an advantageous manner. For instance, the wear behavior on the surface and/or the uppermost layers of the hard material layer can be adjusted such that an advantageous run-in behavior is achieved, while lower-lying areas of the hard material layer are formed by suitable embedding of the DLC phases such that a permanently advantageous wear behavior is achieved.

Preferred developments of the method according to the invention are described in the further claims.

For the hard material coating, a thickness of at least 10 pm is preferred. The DLC embeddings can thus be provided in the scope that is advantageous for the properties. At the same time, a layer of the aforementioned thickness allows the provision of a run-in layer on the upper side and further layers with specific properties in lower positions.

It is furthermore preferred for the hard material coating to contain nitrides of elements of the 4^(th) and/or 5^(th) and/or 6^(th) subgroup of the periodic table, or even to entirely consist of these. Particularly advantageous properties could be found with the aforementioned elements. A hard material coating of chromium nitride (CrN) is particularly preferred.

This similarly applies with regard to the thermal resistance and/or scuff resistance, which can be improved in the hard material coating according to the invention in that the hard material coating comprises further elements such as, e.g., boron, carbon, oxygen and/or silicon.

The embedded DLC phases can be uniformly distributed. In particular, a phase content between 0.1 and 99.9% can be present in relation to the hard material phase.

As an alternative and/or as a supplement in some areas, the DLC embeddings can be localized such that they have a local phase content of 100% and can in particular constitute a layer of 100% DLC embeddings. Dependent on the requirements, good properties could be found for both of the aforementioned embodiments.

As mentioned above, the phase content of the DLC phases can be varied via the layer thickness of the hard material layer, preferably via one or more gradients. Thus, the properties of the coating can be varied as a whole along the thickness and can be adapted particularly well to the requirements in each case.

It has proved to be particularly advantageous to increase the phase content of the DLC phase on the surface and/or in the uppermost 1 to 2 μm of the hard material layer as compared to the remaining coating. This improves the run-in behavior in an advantageous manner.

The aforementioned object is furthermore solved by the sliding element described in claim 10. The preferred embodiments and the advantages that can be obtained thereby correspond to those which have been described above with reference to the method according to the invention. 

1-18. (canceled)
 19. A method for coating a sliding element in which DLC phases are embedded during the deposition of a hard material layer in the hard material layer, wherein the phase content of the DLC phases is increased on the surface andior in the uppermost 1 to 2 μm of the hard material layer as compared to the remaining layer.
 20. The method of claim 19, wherein the sliding element is selected to be a piston ring or a cylinder liner for an internal combustion engine.
 21. The method according to claim 20, wherein the hard material layer is deposited with a thickness of ≧10 μm.
 22. The method according to claim 20, wherein the hard material layer contains nitrides o elements of the 4th and/or 5th and/or 6th subgroup of the periodic table.
 23. The method according to claim 22, wherein the hard material layer furthermore contains at least one additional element selected from the group consisting essentially of: boron, carbon, oxygen and/or silicon.
 24. The method according to claim 20, wherein the embeddings are uniformly distributed.
 25. The method according to claim 20, wherein the DLC phases have a phase content between 0.1 and 99.9%.
 26. The method according to claim 20, wherein the DLC phases have a local phase content of up to 100%.
 27. The method according to claim 20, wherein the phase content of the DLC phases is varied via the layer thickness.
 28. A sliding element with ah a hard material layer comprising embedded DLC phases, wherein the phase content of the DLC phases is increased on the surface and/or in the uppermost 1 to 2 μm of the hard material layer as compared to the remaining layer.
 29. The sliding element of claim 28 comprising a piston ring or a cylinder liner for an internal combustion engine.
 30. The sliding element according to claim 29, wherein the hard material layer has a thickness of
 31. The sliding element according to claim 29, wherein the hard material layer contains nitrides of elements of the 4th and/or 5th and/or 6th subgroup of the periodic table.
 32. The sliding element according to claim 31, wherein the hard material layer furthermore contains at least one additional element selected from the group consisting essentially of: boron, carbon, oxygen and/or silicon.
 33. The sliding element according to claim 29, wherein the embeddings are uniformly distributed.
 34. The sliding element according to claim 29, wherein the DLC phases have a phase content between 0.1 and 99.9%.
 35. The sliding element according to claim 29, wherein the DLC phases have a local phase content of up to 100%.
 36. The sliding element according to claim 29, wherein the DLC phases have a phase content that varies via the layer thickness. 